Ceramic Roller

Instructions：

     In order to make the ceramic rollers to achieve the ideal using effects, extend the service life,

 please refer to the following instructions:

1、Before using, the new roller should be placed in the kiln crown to dry 24 hours or more

 (60-80 ° C).

2、The roller coated with paint should be placed in the kiln crown to dry more than 72 hours .

3、Replace rollers,should be promptly , fast, at the same time rotate the rollers.

4、The rollers from the medium or high temperature zone,to avoid exposure to

 cold items, should be placed in 

the bracket with asbestos cushion and maintain the spin state below 600 ℃.

5、The roller surface with small area glaze particles will affect the of the  thermal shock 

resistance, and it should be cleaned regularly.

6、Substandard raw materials, fuel should be used cautious because it will erode the roller.

理化指标名称 ITEM		HY-A	HY-B	HY-C
氧化铝含量 Alumina	%	75	73	71
吸水率 Water Absorption	%	7	8	9.5
抗弯强度 Flexure Strength	Mpa	≥82	≥68	≥55
体积密度 Bulk Density	g/cm3	≥2.7	≥2.6	≥2.5
热膨胀系数 Thermal Expansivity	×10-6/℃	5.7	5.5	5.3
最高使用温度 Temperture	℃	1300	1200	1160